CONCLUSIONS

Microscopy results suggested that hydrogen served two roles in the fracture of welds: hydrogen promoted the nucleation of microcracks along the dendritic and nitride structures, and hydrogen accelerated the link-up of microcraks by facilitation localized deformation.

REFERENCE

1. Fukuyama S., Zhang L. and Yokogawa K. Hydrogen environment embrittlement of metals in high-pressure hydrogen storage. – Proc.ICF-11.-20-25 March 2005. – Turin, Italy.
2. Chuan-Ming Tseng, Wen-Ta Tsai. Environmentally assisted cracking behavior of single and dual phase stainless steels in hot chloride solutions. Science Direct 12 November 2003, p. 162 -170.
3. Robinson S.I., Somerday B.P., Moody N.R. Hydrogen embrittlement of stainless steels. Proc. ICF-11.- 20-25 March 2005. –Turin, Italy./ Paper № 5638.
4. Chuan-Ming Tseng, Horng-Yih Liou, Wen-Ta Tsai. The influence of nitrogen content on corrosion fatigue crack growth behavior of duplex stainless steel. Materials Science 28 May 2002, p. 190 – 200.
5. Balitskii A., Diener M., Harzenmoser M., Kostyuk I., Kochmanski P., Kolesnikow V., Ostaf V. Crack resistance of high-nitrogen Cr-Mn austenitic steel welded joints / Fracture Mechanics of Materials and Structural Integrity. –Issue 3. – 2004. – p. 647-652.
6.  Balitskii A.I., Kostyuk I., Kolesnikow V.Kubicki J., Medvid A.G., Ostaf V.Yu. Hydrogen induced changes of physical and mechanical properties of materials for power generation and transport equipment // Hydrogen Treatment of Materials (Proceedings of the Fourth International Conference “HTM-2001”, Donetsk-Svyatogorsk, May 17-21, 2004). – Council of Interparlimentary Assembly of States-Participants of Concord of Independent States. – Donetsk. – 2004. – p. 508-512.
7.  Krzysztof Dudziński, Włodzimierz Dudziński, Lidia Pękalska, Grzegorz Pękalski. Spawanie i regeneracyjna obróbka cieplna korpusów turbin parowych. Inzynieria Materialowa 6/2003. P. 712 -715.
8. Anna Rehmus-Forc. Roman Wielgosz. Zastosowanie żaroodpornych stopów niklowych w turbinach parowych. Inzynieria Materialowa 6/2003, p. 361 -634. // Rehmus-Forc A. ,Wielgosz R. // Use of heat-resisting nickel alloys in gas turbines // II Krajowa Konferencja "Nowe Materiały - Nowe Technologie w Przemyśle Okrętowym i Maszynowym", Międzyzdroje 2003.
9. Maria Sozanska, Katarzyna Klyk-Spyra, Joanna Lasota Korelacja pomiędzy ilościowym opisem mikrostruktury, a właściwościami mechanicznymi w stali duplex w obecności wodoru. Inzynieria Marialowa 6/2003. P. 369 – 372. (Sozańska M., Kłyk-Spyra K., Lasota J.). II Krajowa Konferencja "Nowe Materiały - Nowe Technologie w Przemyśle Okrętowym i Maszynowym", Międzyzdroje 2003 // Correlation between structural and mechanical properties in the duplex steel in the presence of hydrogen.  
10. Walenty Jasinski. Analiza fazowa materiału rur katalitycznych reformerów amoniaku. Phase analysis of material of centrifugal casted catalytic pipes. Inzynieria Materialowa ROR XXIV, p. 306 – 309.

Balitskii A., Ivaskevich L., Kostyuk I., Kochmanski P., Kolesnikow V., Ostaf V. // Hydrogen embrittlement of welded joints of Cr–Mn austenitic steels. Водневе окрихчення зварних зєднань Cr–Mn аустенітних сталей // Проблеми корозії та протикорозійного захисту матеріалів. Problems of corrosion and protection of materials  Physicochemical mechanics of materials.– Special issue. - N 5, vol.1, 2006. – P. 233-235.

Balitskii A., Ivaskevich L., Kostyuk I., Kochmanski P., Kolesnikov V., Ostaf V. // Hydrogen embrittlement of welded joints of Cr–Mn austenitic steels Водневе окрихчення зварних зєднань Cr–Mn аустенітних сталей // Проблеми корозії та протикорозійного захисту матеріалів. Problems of corrosion and protection of materials Physicochemical mechanics of materials. – Special issue. - N 5, vol.1, 2006. – P. 233-235.

https://www.researchgate.net/publication/357084703_Balitskii_A_Ivaskevich_L_Kostyuk_I_Kochmanski_P_Kolesnikow_V_Ostaf_V_Hydrogen_embrittlement_of_welded_joints_of_Cr-Mn_austenitic_steels_Vodneve_okrihcenna_zvarnih_zednan_Cr-Mn_austenitnih_stalej_Probl